SUPERNOVA 316 Slickline
SUPERNOVA 316 Slickline
With its combination of high break loads and good pitting and crevice corrosion resistance, Supernova 316® is a cost-effective solution for less corrosive oil and gas wells with zero H2S.
Manufactured in Switzerland and certified to 9001: 2008 all Supernova Slicklines are fully traceable, 100% Weld Free, 100% Eddy Current Tested and Wrap Tested.
All are produced with a consistent, tightly controlled surface finish, wire helix and wire cast for optimal spooling and in-service performance.
SUPERNOVA 316 Slickline
With its combination of high break loads and good pitting and crevice corrosion resistance, Supernova 316® is a cost-effective solution for less corrosive oil and gas wells with zero H2S.
Manufactured in Switzerland and certified to 9001: 2008 all Supernova Slicklines are fully traceable, 100% Weld Free, 100% Eddy Current Tested and Wrap Tested.
All are produced with a consistent, tightly controlled surface finish, wire helix and wire cast for optimal spooling and in-service performance.
Key Characteristics
- Good general corrosion resistance in wells with medium concentrations of CO2 (up to 30%) and low chlorides (up to 2.5%) with both moderate Bottom Hole Temperatures and Pressures and no H2S
- Excellent resistance to general corrosion
- High break loads due to high tensile strength
- May be used in temperatures up to 150°C in less corrosive environments
- Subject to pitting and crevice corrosion in warm chloride environments and to stress corrosion cracking above 60°C
- An economical option where carbon (plow) slicklines may fail due to corrosion
- Not recommended for wells containing H2S
Key Characteristics
- Good general corrosion resistance in wells with medium concentrations of CO2 (up to 30%) and low chlorides (up to 2.5%) with both moderate Bottom Hole Temperatures and Pressures and no H2S
- Excellent resistance to general corrosion
- High break loads due to high tensile strength
- May be used in temperatures up to 150°C in less corrosive environments
- Subject to pitting and crevice corrosion in warm chloride environments and to stress corrosion cracking above 60°C
- An economical option where carbon (plow) slicklines may fail due to corrosion
- Not recommended for wells containing H2S
Key Data
Standard Diameter (Inches) | Min Breaking Load (lbf) | Min Tensile (N/mm2) (Ksi) | Nominal Weight (lbs/ 1000ft) | Minimum Slickline Stretch (Inch/100ft/ 100lb) | Minimum Sheave Diameter (Inches) | |
0.092 | 1420 | 1460 | 214 | 22.64 | 0.83 | 11 |
0.108 | 1940 | 1440 | 212 | 31.20 | 0.60 | 13 |
0.125 | 2530 | 1420 | 206 | 41.80 | 0.45 | 15 |
0.140 | 3130 | 1410 | 203 | 53.00 | 0.36 | 17 |
0.160 | 4050 | 1380 | 202 | 69.00 | 0.22 | 20 |
Chemical Composition
Element | C | Si | Mn | P | S | Cr | Mo | Cu | Ni | N | |
Weight % | Min | – | – | – | – | – | 16.50 | 2.00 | – | 10.00 | 0.03 |
Max | 0.08 | 1.00 | 2.00 | 0.045 | 0.030 | 18.00 | 2.60 | – | 13.80 | 0.06 |
Corrosion Resistance PRE Number (PRE)
PRE = Chromium + 3.3 x Molybdenum + 16 x Nitrogen.